Electrolytic etching of AZ91D Mg alloy in AlCl3-EMIC ionic liquid for the electrodeposition of adhesive Al coating
Electrolytic etching of AZ91D Mg alloy in AlCl3-EMIC ionic liquid for the electrodeposition of adhesive Al coating

作者:Xu, BJ (Xu, Bajin)1 ] Zhang, M (Zhang, Min)1 ] Ling, GP (Ling, Guoping)1 ]

 

SURFACE & COATINGS TECHNOLOGY

 

卷: 239

 

页: 1-6

DOI: 10.1016/j.surfcoat.2013.11.003

出版年: JAN 25 2014

查看期刊信息

摘要

In this paper, electrolytic etching pretreatment of AZ91D Mg alloy in AlCl3-1-ethyl-3-methyl-imidazolium chloride (AlCl3-EMIC) ionic liquid was employed for the electrodeposition of well adhesive Al coatings. The quantitative measurement of coating adhesion was carried out and the mechanism ofelectrolytic etching on the improvement of coating adhesion was studied through Scanning Electron Microscopy (SEM), energy dispersive X-ray (EDS), X-ray Photoelectron Spectroscopy (XPS) and Grazing Incidence X-ray Diffraction (GIXRD). With electrolytic etching pretreatment at 25 mA/cm(2), the adhesion of subsequently electrodeposited Al coatings on AZ91D was higher than 4 MPa. The improvement of adhesion strength was attributed to both the complete removal of oxide layers on the surface and the uniform dissolution of Mg solid solution phase (alpha phase) and intermetallic phase Mg17Al12 (beta phase). Meanwhile, further electroless replacement of metallic Al was observed at the position of alpha phase. In the case of 5 mA/cm(2)electrolytic etching pretreatment, only partial surface oxide layers were removed and etching grooves formed on the surface, which resulted in a low adhesion strength of 0.51 MPa. (C) 2013 Elsevier B.V. All rights reserved.

作者信息

通讯作者地址: Ling, GP (通讯作者)

Zhejiang Univ, Dept Mat Sci & Engn, Hangzhou 310027, Peoples R China.

 

地址:

[ 1 ] Zhejiang Univ, Dept Mat Sci & Engn, Hangzhou 310027, Peoples R China

 

电子邮件地址:linggp@zju.edu.cn

基金资助致谢
基金资助机构 授权号
National Natural Science Foundation of China 
51271166